Bare corrosion resisting chromium-nickel-molybdenium welding rods for welding of austenitic stainless alloys of 18% Cr - 8% Ni and 18% Cr - 10% Ni - 3% Mo-types.
OK Tigrod 316L has a good general corrosion resistance, particularly against corrosion in acid and chlorinated environments.
The alloy has a low carbon content which makes it particularly recommended where there is a risk of intergraular corrosion.
The alloy is widely used in the chemical and food processing industries as well as in shipbuilding and various types of architectural structures.
| Impact Value | Testing Temperature | |||
| As Welded | ||||
| 120 J (89 ft-lb) | -110 degC (-166 degF) | |||
| 75 J (56 ft-lb) | -196 degC (-321 degF) | |||
| 130 J (96 ft-lb) | -60 degC (-76 degF) | |||
| 175 J (130 ft-lb) | 20 degC (68 degF) | |||
| Condition | Elongation | Tensile Strength | Yield Strength |
| As Welded | 32 % | 600 MPa (87 ksi) | 470 MPa (68 ksi) |
| Wire Electrode | Werkstoffnummer : ~1.4430 SFA/AWS A5.9 : ER316L EN ISO 14343-A : W 19 12 3 L |
| Approvals | ABS ER 316L BV 316L BT CE EN 13479 CWB ER316L DNV-GL VL 316 L (I1) NAKS/HAKC 1.6 - 3.2 mm VdTÜV 04270 |
| Approvals are based on factory location. Please contact ESAB for more information. |
| Alloy Type | Austenitic (with approx. 10 % ferrite) 19% Cr - 12% Ni - 3% Mo - Low C |
| Typical Wire Composition % | ||||||||||||||
| C | Cr | Cu | FN WRC-92 | Mn | Mo | N | Ni | P | S | Si | ||||
| 0.01 % | 18.2 % | - | 7 % | 1.7 % | 2.6 % | 0.04 % | 12.0 % | - | - | 0.4 % | ||||
| Typical Weld Metal Analysis % | ||||||||||||||
| 0.01 % | 19 % | 0.1 % | - | 1.8 % | 2.6 % | - | 12 % | 0.02 % | 0.01 % | 0.4 % | ||||